Verifying the Quality of Coating Installation–Post-Application Quiz
Quiz Summary
0 of 30 Questions completed
Questions:
Information
You have already completed the quiz before. Hence you can not start it again.
Quiz is loading…
You must sign in or sign up to start the quiz.
You must first complete the following:
Results
Results
0 of 30 Questions answered correctly
Your time:
Time has elapsed
You have reached 0 of 0 point(s), (0)
Earned Point(s): 0 of 0, (0)
0 Essay(s) Pending (Possible Point(s): 0)
Categories
- Post Application: Adhesion 0%
- Post Application: Hardness 0%
- Post Application: Holiday Detection 0%
- 1
- 2
- 3
- 4
- 5
- 6
- 7
- 8
- 9
- 10
- 11
- 12
- 13
- 14
- 15
- 16
- 17
- 18
- 19
- 20
- 21
- 22
- 23
- 24
- 25
- 26
- 27
- 28
- 29
- 30
- Current
- Review
- Answered
- Correct
- Incorrect
-
Question 1 of 30
1. Question
Category: Post Application: Holiday DetectionIn terms of coating performance, a holiday is:
CorrectIncorrect -
Question 2 of 30
2. Question
Category: Post Application: Holiday DetectionWhich of the following is a common cause of pinholes in a coating?
CorrectIncorrect -
Question 3 of 30
3. Question
Category: Post Application: Holiday DetectionWhat is the coating thickness threshold that determines whether low voltage or high voltage holiday detection is used?
CorrectIncorrect -
Question 4 of 30
4. Question
Category: Post Application: Holiday DetectionFor holiday detection to be used successfully, the coating must be:
CorrectIncorrect -
Question 5 of 30
5. Question
Category: Post Application: Holiday DetectionFor holiday detection to be used successfully, the substrate must be:
CorrectIncorrect -
Question 6 of 30
6. Question
Category: Post Application: Holiday DetectionWhat type of water is recommended to be used to saturate the sponge on a low voltage holiday detector?
CorrectIncorrect -
Question 7 of 30
7. Question
Category: Post Application: Holiday DetectionHow does an operator verify continuity of a low voltage (wet sponge) holiday detector?
CorrectIncorrect -
Question 8 of 30
8. Question
Category: Post Application: Holiday DetectionWhat is the thickness threshold of a coating that would require a wetting agent to be added to the water?
CorrectIncorrect -
Question 9 of 30
9. Question
Category: Post Application: Holiday DetectionWhat factor determines the test voltage for inspecting a coating using a high voltage holiday detector?
CorrectIncorrect -
Question 10 of 30
10. Question
Category: Post Application: Holiday DetectionCalculate the correct voltage setting for inspecting a 60-mil lining using a high voltage holiday detector.
CorrectIncorrect -
Question 11 of 30
11. Question
Category: Post Application: Holiday DetectionAccording to ASTM D5162, what is the maximum rate that the wetted sponge or electrode is scanned across the coated surface?
CorrectIncorrect -
Question 12 of 30
12. Question
Category: Post Application: HardnessWhat is the primary purpose of testing the hardness of a coating on a pipe?
CorrectIncorrect -
Question 13 of 30
13. Question
Category: Post Application: HardnessWhat type of Durometer is typically used to test thick film epoxy pipe coatings?
CorrectIncorrect -
Question 14 of 30
14. Question
Category: Post Application: HardnessWhen testing the hardness of a coating using a Durometer, what unit of measure is used?
CorrectIncorrect -
Question 15 of 30
15. Question
Category: Post Application: HardnessWhich of the following is used to verify the accuracy of a Durometer prior to use?
CorrectIncorrect -
Question 16 of 30
16. Question
Category: Post Application: HardnessWhat is the minimum number of hardness readings to obtain per area?
CorrectIncorrect -
Question 17 of 30
17. Question
Category: Post Application: HardnessTrue of False: ASTM provides a hardness value correction table based on the prevailing surface temperature and relative humidity at the time of testing.
CorrectIncorrect -
Question 18 of 30
18. Question
Category: Post Application: AdhesionTrue or False: Tensile adhesion is also considered “pull-off” adhesion.
CorrectIncorrect -
Question 19 of 30
19. Question
Category: Post Application: AdhesionTrue or False: Shear adhesion is also considered “pull-off” adhesion.
CorrectIncorrect -
Question 20 of 30
20. Question
Category: Post Application: AdhesionA distinct break between coating layers or between the substrate and first coating layer is called a/an:
CorrectIncorrect -
Question 21 of 30
21. Question
Category: Post Application: AdhesionA break within a coating layer is called a/an:
CorrectIncorrect -
Question 22 of 30
22. Question
Category: Post Application: AdhesionTrue or False: According to ASTM D4541, when testing the adhesion of coatings on steel, the operator must always test the coating to the point where it fractures.
CorrectIncorrect -
Question 23 of 30
23. Question
Category: Post Application: AdhesionWhy is scoring the coating not recommended for thin film coatings?
CorrectIncorrect -
Question 24 of 30
24. Question
Category: Post Application: AdhesionWhat situation may require scoring of the coating prior to pull-off adhesion testing?
CorrectIncorrect -
Question 25 of 30
25. Question
Category: Post Application: AdhesionWhich of the following is not an alignment process used by pull-off adhesion testers?
CorrectIncorrect -
Question 26 of 30
26. Question
Category: Post Application: AdhesionWhich of the following is not a method of applying tensile force using portable adhesion testers?
CorrectIncorrect -
Question 27 of 30
27. Question
Category: Post Application: AdhesionThe most common diameter loading fixture for determining the pull-off adhesion of coatings on steel is:
CorrectIncorrect -
Question 28 of 30
28. Question
Category: Post Application: AdhesionWhat is the maximum pull-off rate in psi/second specified by ASTM D4541?
CorrectIncorrect -
Question 29 of 30
29. Question
Category: Post Application: AdhesionWhat is the minimum number of replicates per area prescribed by ASTM D4541 to characterize the adhesion properties of a coating?
CorrectIncorrect -
Question 30 of 30
30. Question
Category: Post Application: AdhesionTrue or False: According to ASTM D6677, the adhesion properties of a coating can be evaluated using a utility knife blade and a rating scale.
CorrectIncorrect